SEQUENZATZUNG ZUR PHASENIDENTIFIZIERUNG IN TECHNISCHEN AlZnMgCu- 
LEGIERUNGEN 
R. Poganitsch, L. Sigl und F. Jeglitsch, Montanuniversitat Leoben, 
Österreich 
Summary 
Sequential Etching for the Identification of Phases in Technical 
AlZnMgCu-Alloys 
The investigation deals with the identification of the intermetallic 
phases occuring in technical AlZnMgCu-alloys. The composition of the 
AlZnMgCu-phases was determined by EDX-analysis. From the percentages 
of the individual elements a combined parameter was formulated to 
identify the phases TalznMgcu and Ma1znMgCu® Based on the results of 
microprobe analyses an etching procedure is proposed, which allows 
to identify the phases T, M, S, 6, N and Al,Fe in a sequence of etching 
steps. The phases are attacked one after another. 
Einleitung 
Ein typischer Vertreter der hochfesten AlZnMgCu-Legierungen ist die 
Legierung 7075, deren nominelle Zusammensetzung in Bild 1 wiederge- 
geben ist. Die Hauptlegierungselemente Zn, Mg und Cu tragen die Aus- 
hdrtung. Die Elemente Fe, Si und Ti sind Verunreinigungen, die ange- 
gebenen Gehalte stellen Maximalwerte dar. Die Ubergangsmetalle Mn, Cr 
und Zr werden als Zusatzelemente in Mengen von einigen Zehntel Masse-% 
beigegeben. Die Verunreinigungselemente und ein gewisser Anteil der Zu- 
satzelemente werden in Aluminium in schwer 16slichen Phasen abgebunden. 
Dieser Beitrag beschäftigt sich mit der Identifizierung der im Legie- 
rungstyp AlZnMgCu auftretenden Phasen. Die eigenen Untersuchungen er- 
folgten an Versuchslegierungen der Zusammensetzung 
Al - 6.3%Zn - 2.3%Mg - 1.0 bls 2.32Cu - 0.11%Zr - 0.10% Pe — 0.07281 - 
0.03%Ti. 
Das Vierstoffsystem Al-Zn-Mg-Cu (Bild 1) zeigt die Einphasenräume bei 
460°C (1) und die ungefähren Zusammensetzuncgen der Phasen S und 6 bzw. 
für T, M und Z die Endkonzentrationen der Mischkristallreihen. Die 
115