SUBSTRUCTURE CHARACTERISTICS OF TiNi SHAPE MEMORY 
ALLOYS 
Peter Filip and Albert C.Kneissl* 
Institute of Materials Engineering, Technical University Ostrava, Czech Republic 
* Institute of Physical Metallurgy and Materials Testing, University of Leoben, Austria 
Abstract 
The substructure of several TiNi shape memory alloys has been analysed by using of TEM in the 
annealed, work hardened and trained condition. The self-accomodation triangular morphology of 
B19' martensite is typical for the annealed alloys. After training processes and after cyclic thermal 
loading of TiNi elements, the substructure changes markedly. After this treatment a very high 
dislocation density has been detected and the martensitic variants preferentially have the same 
orientation relationship to the B2 high-temperature phase as in the annealed specimens. 
Furthermore "ghost martensite" has been observed in specimens cycled for more than 10* times. 
This phenomenon is connected with the two way shape memory effect. 
SUBMIKROSKOPISCHE GEFUGEUNTERSUCHUNGEN IN TiNi- 
FORMGEDA CHTNISLEGIERUNGEN 
Kurzfassung 
Das submikroskopische Gefiige mehrerer TiNi-Formgedichtnislegierungen im gegliihten, 
kaltverformten und trainierten Zustand wurde mittels Transmissionselektronenmikroskopie 
untersucht. Die dreieckige Morphologie in den gegliihten Proben ist typisch fiir die Selbst- 
Akkommodation des B19'-Martensits. Nach dem Trainieren und nach weiterer zyklischer, 
thermischer Belastung steigt die Versetzungsdichte sehr stark an, wobei die Vorzugsorientierung 
der Martensitvarianten in Bezug auf die Hochtemperaturphase B2 sehr ähnlich dem gegliihten 
Zustand ist. In Proben, die über 10000 thermische Zyklen erfahren haben, findet man nur mehr 
die Spuren ("ghost martensite") des ehemaligen Martensits. Trotzdem gibt es auch hier noch den 
Zweiwegformgedéichtniseffekt. 
Prakt. Met. Sonderbd. 26 (1995) 201